Three-dimensional printing of strontium-containing mesoporous bioactive glass scaffolds with varied macropore morphologies: an in vitro cytological experiment
Zhang Xu
Wu Liang-hao
Li De-jian
Ao Rong-guang
Chen Fan-cheng
Yu Bin
Yu Bao-qing
Abstract：BACKGROUND:Macropore morphology of a composite scaffold prepared by the three-dimensional printing technique is of great importance in determining the physicochemical and biological properties of tissue engineering scaffolds.OBJECTIVE:To fabricate strontium-containing mesoporous (Sr-MBG) bioactive glass (PCL) scaffolds by the three-dimensional printing technique, and to explore the effect of these scaffolds on MC3T3-E1 proliferation and osteogenic differentiation, thereby to find out the optimal macropore morphology.METHODS: Sr-MBG/PCL composite scaffolds were fabricated by the three-dimensional printing technique. The angles between fibrous latitudes and longitudes were set to 45°, 60° and 90°. Then the proliferation and alkaline phosphatase activity of MC3T3-E1 cells on the scaffolds were tested.RESULTS AND CONCLUSION: Cell counting kit-8 results showed that MC3T3-E1 cells could proliferate on all the three kinds of scaffolds. The proliferation rate of MC3T3-E1 cells on the 45° Sr-MBG/PCL scaffolds was just slightly higher than that on the 60° and 90° Sr-MBG/PCL scaffolds at days 1 and 4 (P > 0.05), but there was a significant increase at day 7 (P < 0.05). The 45° Sr-MBG/PCL scaffolds exhibited a significant increase in alkaline phosphatase activity of MC3T3-E1 cells compared to the 60° and 90° Sr-MBG/PCL scaffolds at day 14 (P < 0.05), while there was no significant difference among three groups at day 21 (P > 0.05). These results indicate that the 45° Sr-MBG/PCL scaffold is more suitable to promote the proliferation and osteogenic differentiation of the MC3T3 cells than the 60° and 90° Sr-MBG/PCL scaffolds.
Keywords：Biocompatible MaterialsStrontiumOsteoblastsCell ProliferationAlkaline PhosphataseTissue Engineering
Publication Date：2017-01-01
Online Publishing Date：2025-08-15(First online date of this platform, not the publication date of the document)
Pages：6( 2858-2863 )